Although Nd:YAG was invented in the Sixties last century, it has been and is still the most commonly used solid-state crystal material. Nd:YAG crystals are wildly used in all types of solid-state lasers systems-frequency-doubled continuous wave, high-energy Q-switched, and so forth.
Its good fluorescent lifetime thermal conductivity and physical strengths makes it suitable for high power lamp pumped laser.
|
1)
|
Nd Dopant Concentration:
|
0.5-1.2 atm%tolerance within 10% of concentration
|
|
2)
|
Diameter:
|
3 ~ 14mm
|
|
3)
|
Length:
|
1~ 160mm
|
Typical Specification and Tolerance:
|
1) |
Orientation:
|
<111> crystalline direction (+/-0.5℃)
|
|
2)
|
Wavefront Distortion:
|
<l/10 at 632.8nm for 3 ~ 7mm <l/8 per inch at 632.8nm for >=7mm |
|
3)
|
Surface Quality:
|
better than 20/10 Scratch/Dig per MIL-O-1380A
|
|
4)
|
Parallelism:
|
< 10 arc seconds
|
|
5)
|
Perpendicularity:
|
< 5 arc minutes
|
|
6)
|
Surface Flatness:
|
<l/10 at 632.8nm
|
|
7)
|
Clear Aperture:
|
Central 90%
|
|
8)
|
Chamfer:
|
0.15x45o
|
|
9)
|
Damage Threshold:
|
> 15J/cm2(uncoated ) > 700 MW/cm2(coated) |
|
10)
|
Coatings:
|
a)AR@1064nm, R<0.1%; (see coating 9-1) b)AR@1064nm, R< 0.1%;HT@808nm, T>95%;(see coating 6-2) c)HR@1064nm, R>99.8%; HT@808nm, T>95%;(see coating 9-2) d)HR@1064nm, R>99.8%; HT@808nm, T>95%; HR@532nm, R>99%;(see coating 9-3) |
To inquiry or order a finished Nd:YAG laser rod, please specify the specification listed above, for common application, we only need to know the main specification: Nd-dopant concentration, sizes, and coating. For special request, please specify specification in details for evaluation and fabrication.
Physical and Optical Properties
| Chemical Formula | Nd:Y3A15O12 |
| Crystal Structure | Cubic |
| Lattice Constants | 12.01Ä |
| Concentration | ~ 1.2 x 1020 cm-3 |
| Melting Point | 1970 °C |
| Density | 4.56 g/cm3 |
| Mohs Hardness | 8.5 |
| Refractive Index | 1.82 |
| Thermal Expansion Coefficient | 7.8 x 10-6 /K [111], 0 - 250 °C |
| Thermal Conductivity | 14 W/m /K @20 °C, 10.5 W /m /K @100 °C. |